Migration-free size for glass fibers

ABSTRACT

A migration-free size for glass fibers which includes a silane coupler, lubricant and film former and is characterized by the absence of a carrier, either aqueous or organic. To provide required shelf-life, a volatile agent such as acetone is added in limited amount to block coupler-film former reaction pending use of the size.

This is a division of application Ser. No. 162,854, filed June 25, 1980, now U.S. Pat. No. 4,455,400, issued June 19, 1984.

BACKGROUND

Glass fibers are now produced for use in a broad variety of technologies. Their production involves a procedure wherein molten glass is passed through a multiple orificed bushing at a relatively high rate. As the very small nascent glass streams extend from the bushing, they encounter a "prepad" or cooling stage usually provided as a water spray. The cooled and now rigidified "filaments" then encounter a "pad" or size applicator at which point they are coated with a protective film, following which the coated filaments are brought together at a "gathering shoe" to form a "strand". This strand is coiled upon a spool to form a "package". During formation of the package, the strand is traversed back and forth across the spool by a spooling cam driven device or the like, often referred to as a traverse. The spool is rotated at a collet or winder and the tension exerted upon the strand by the winding activity serves to attenuate the molten stream of glass passing immediately from the bushing.

The above-described sizing procedure is highly important to the successful production of strand as well as to the formation of the great variety of products utilizing glass fibers. In this regard, when considered in isolation, glass filaments have a relatively high theoretical strength. However, in the course of their formation to strand and subsequent glass fiber products, such strength is not realized, due at least in part to minute defects developed upon filament surfaces occasioned by glass on glass abrasion during production. A highly important function of the sizing procedure therefore, is to impart a desired degree of lubricity to the filaments, thus lessening this abrading phenomena. Filament degradation further may be influenced by the water content of sizes with which they are coated, the most conventional of sizes being provided as aqueous solutions or emulsions. See in this regard, U.S. Pat. No. 3,473,950.

Another important function of the size coating stems from the nature of the glass filament surfaces. These surfaces are very smooth and are highly hydrophilic in nature. In consequence, a thin film of water tends to form upon the filament surfaces functioning to disrupt any bond, chemical or physical, which would otherwise be formed between the glass and the material within which it may be embedded. Accordingly, in addition to the above described lubricant, the size generally will incorporate a coupling agent serving to react both with the silica in the glass as well as with organic matrix material within which the filaments and strands usually are embedded. As is apparent, the selection of coupling agent looks to the ultimately intended use of the fiber, a compatible coupling agent of one variety being utilized with elastomers and the like, while that of another variety being utilized with glass fiber reinforced resinous articles and the like.

Film formers provide the final principal active ingredient of the sizes and are selected as resins of relatively higher molecular weight, for example epoxy resins and the like. The film formers serve in effect to provide a tougher film coating which, for many applications of the glass fibers, imparts a necessary integrity or character to strand. For example, where the strand is utilized as roving for weaving glass fiber reinforcing sheets and the like, a certain stiffness is required of the product to permit its manipulation by the ultimate user in connection with placement within molds and the like. The strand stiffness translates into the woven integrity of the cloth to permit its facile manipulation. Of course, the selection of the stiffness quality must be such as to derive adequate cloth integrity while still permitting manipulation of the cloth about the corners of a mold or the like within or upon which it is utilized.

In general practice, the coupling agent, lubricant and film former are applied to the glass filaments utilizing the media of a water carrier. In this regard, the combined "solid" ingredients represent about 5% by weight of the liquid size which is continuously recirculated at the applicator stage from a supply reservoir. Following application of the size, the formation of strands and development of a package as above described, the package is then moved to a drying oven at which point the aqueous or volatile carrier phase of the size is driven off.

To avoid the possibility of attack upon the glass surfaces by the aqueous phase of the sizes, investigators have developed organic carriers or non-aqueous polar solvents as carriers, for example as described in U.S. Pat. No. 3,473,950. Generally, the steps in producing filaments using such sizes follow that described, including the step of heating the completed packages to drive off the volatile organic carrier. In all systems, the carrier represents the major component of the size solution, the solids or coupling agent, lubricant and film formers representing, as noted, about 5% by weight of the material.

A principal difficulty encountered by industry in the utilization of sizes resides in a phenomenon termed "migration". As noted above, the liquid carrier phase of the size is driven off by depositing the strand package in an oven. Inasmuch as these packages typically are cylindrical in form, being wound upon a cardboard collar, the vaporization of the liquid phase takes place somewhat differentially or progressively from the outside and inside faced surfaces as well as the edge surfaces toward the central portion of the package. As the carrier, i.e. volatile constituent, is removed to a point wherein a total 10 to 12 percent moisture content for the package is present, it is opined that migration of the internally disposed carrier toward the outward surfaces commences by capillary action. This causes a movement of the solids component of the size from the position of its initial deposition toward the surface of the package. Such movement of important constituents may result in the development of randomly located regions of the filaments exhibiting an inadequate size coating. Further, there develops an excess accumulation of these important constituents at the externally exposed surfaces of the package.

As indicated earlier, as strand is wound to form a package, it is manipulated in a back and forth fashion through the use of a traverse. Such spool winding techniques necessarily provide for spaced "turn around" points along the length of each strand. These points represent the strand position at the opposed edges of the cylindrical package wherein the traverse reverses direction of strand. In the course of the above-described migration of liquid carrier and concurrent movement of the important size constituents toward the outer edge of the package, a build-up of the latter constituents is evidenced at the outer edge surfaces and this build-up then is witnessed as a series of spaced material build-ups in the strand as it is unwound from the package. When the strand is subsequently drawn from the package and woven to form cloth products and the like, the dispersed turn around points with excess size material become visible and represent an undesirable aspect of the resultant woven product. This particularly is true where drying is carried out in conventional fashion within direct gas fired ovens. Where such drying is utilized, the materials of combustion tend to alter the color of the cationic materials usually incorporated within the size. This spotted discoloration tends to derogate from the quality of the resultant product.

As is apparent, the removal of solid size materials due to migration results in dispersed sites of filament surface area having less size. The thus exposed surface areas may exhibit lowered strength characteristics resulting in dispersed filament breakage which may result in undesired "fuzz" formation. Where the sized strand is intended for application as reinforcement within elastomeric product such as pneumatic tires, driving belts, timing belts and the like, it initially is coated with an impregnant. This impregnant serves the purpose of locking the strands within the elastomer and may have a variety of formulations as described, for example, in U.S. Pat. No. 3,850,872. Inasmuch as the impregnant fails to adhere to regions of the fibers which exhibit an excess coating of size, the quality of anchoring of the strands within the elastomer is adversely affected where materials are utilized evidencing the migration effects. Such condition of the impregnant coated strands is generally referred to in the industry as "streaking".

In addition to the pronounced effects of migration in the course of oven drying of the strand packages, the phenomenon also has been observed to commence early in the process of strand formation. For example, migration due to evaporation has been found to occur as strand packages are maintained in holding or surge areas prior to their introduction to the heating step. This migration is caused by the evaporation of the outer surfaces of the package during that holding interval.

The term "glass fibers", as used herein, shall refer to (1) continuous fibers formed by the rapid attenuation of hundreds of streams of molten glass and to strands formed when such continuous glass fiber filaments are gathered together in forming; and to yarns and cords formed by plying and/or twisting a number of strands together, and to woven and nonwoven fabrics which are formed of such glass fiber strands, yarns or cords, and (2) discontinuous fibers formed by high pressure steam or air directed angularly downwardly onto multiple streams of molten glass issuing from the bottom side of a glass molten bushing and to yarns that are formed when such discontinuous fibers are allowed to rain down gravitationally onto a foraminous surface wherein the fibers are gathered together to form a silver which is drafted into a yarn; and to woven and non-woven fabrics formed of such yarns of discontinuous fibers, and (3) combinations of such continuous and discontinuous fibers in strand, yarn, cord and fabrics formed thereof.

SUMMARY OF THE INVENTION

The present invention is addressed to a size preparation and treatment for glass fibers which achieves a substantial avoidance of migration phenomena. When formulated in accordance with the invention, the sizes are applied in the absence of a carrier, either aqueous or organic. In consequence, the otherwise necessary drying procedures driving off carrier are substantially avoided to eliminate the principal contributive factor to size migration.

As another aspect and object of the invention, it has been discovered that a non-migrating size may be formulated incorporating the principal functional coupling agent, lubricant and film former components of a conventional size in the absence of liquid carrier but with a volatile liquid blocking agent which significantly enhances the shelf life thereof. By so limiting the amount of this blocking agent to about eight percent by weight or less, the volatile constituent subsequently may be driven off by vaporization in the course of strand formation and over a subsequent relatively short heat drying interval. When so driven off, the reaction of coupling agent and film former is permitted to occur, while capillary movement is avoided to, in turn, avoid any migratory movement of the now reacted size components.

As another feature of the invention, it has been discovered that the quantity of size material required to effect a full coating thereof upon glass filaments is significantly reduced as compared to conventional, carrier born sizes. This significant volumetric reduction readily is translatable to lowered energy requirements and production costs.

A further object of the invention is the provision of a new and improved method of coating glass fibers, and particularly glass fibers at forming, wherein the coating material is provided in the absence of an aqueous or organic carrier.

Further objects and advantages of the invention will become apparent to those skilled in the art to which it relates from the following description of the preferred embodiments.

BRIEF DESCRIPTION OF THE DRAWINGS

The single FIGURE is a collection of regression curves showing the hoop stress performance of pipe samples formed with conventionally sized glass fiber as well as pipes formed with glass fiber sized according to the invention.

DETAILED DESCRIPTION

As indicated above, the selection of precise size formulations will be dependent upon the ultimate application or use contemplated for the sized glass fibers. The size applied will incorporate at least a lubricant component to which may be added coupler, film forming components and optionally dyes and/or anti-static agents. Of particular importance, these components are provided in the absence of carrier, either aqueous or organic, a component typically representing the major ingredient of size formulations heretofore employed. Where film former and coupler are included, it is preferred to incorporate a volatile blocking agent in an amount less than about eight percent by weight which, while present within the size, serves to stabilize it by blocking coupler-film former reaction. A considerably improved shelf life for the size is achieved with the blocking agent present therein. The agent is removed to a great extent in the course of package formation, the minor remainder being removed by heating a completed package within an oven. During this heating stage, the volatile blocking agent, by virtue of the controlled amounts thereof within the size formulation, is fully removed from the strand package essentially entirely by a vaporization activity. Such activity, as opposed to capillary movement, is found not to cause the important size components to be driven or migrate toward the surface of the strand package. Of course, where the end utilization permits low moisture processing into an impregnation bath or chop process, no oven drying is required.

In the discourse to follow, various size formulations prepared according to the invention are described initially, following which the discussion turns to tests for certain size systems intended for specific applications, i.e. for use with glass fibers used in woven roving, or suited for embedding within resin structures of a broad variety.

Generally, the size applied will incorporate a lubricant component to which is added a coupler, film forming components and, optionally, dyes and anti-static agents. These components are provided in the substantial absence of carrier, either aqueous or organic. As a consequence of the resultant lower volumes of size utilized, the volatile constituents present on the glass filaments are substantially volatilized prior to package formation. Certain film formers and couplers of size formulations have a tendency to exhibit limited shelf lives; thus, where storage is contemplated, the invention provides for the incorporation of a volatile blocking agent in an amount less than about eight percent by weight which, while present within the size formulation, does not act as a carrier but serves to stabilize the formulation by blocking the reaction of coupler with film former. Considerably improving the shelf life of size when present therein, such blocking agents are found to be quite useful in the most typically encountered production systems wherein size is batch mixed and utilized over a reasonably extended interval. However, where on-line facilities for formulating the size are provided, such blocking agents are not required.

In either approach utilized, the salient aspect of the invention resides in a successful application of effective size without resort to a volatile liquid carrier per se which must be driven off as a subsequent production step, a step which results in unwanted migration phenomena of the solids component of the size. Where a volatile blocking agent formulation is utilized in accordance with the invention, the amount thereof is limited as above indicated to an extent wherein a substantial amount thereof is volatilized in the course of filament and strand formation prior to its reaching the packaging spool. When the resultant package is oven dried, the moisture content thereof is about one to two percent by weight and capillary action causing material solids migration will not be present, the remaining agent and any other volatiles being removed through the mechanism of elementary vaporization.

In addition to the highly advantageous nonmigratory characteristics of the carrier-free size formulations of the invention, other process advantages will be found to accrue through its use, one being that the physical volume of size required in the glass fiber production process is greatly diminished. For example, industrially accepted size formed having about a five percent solids component and the remainder being an aqueous carrier will require application of about 480 gallons thereof at ten typical bushing positions over a 24-hour interval. Similarly, thixotropic size materials will incorporate about 3.5 percent solids and will require application of about 200 gallons over a 24-hour interval for ten bushing positions. Compared with the above, a typical formulation according to the invention, having substantially no carrier, will adequately coat the glass fibers utilizing only a ten-gallon supply over the noted 24 hours at ten positions of application. The lower volumes required for the sizing process permit faster mixing, easier clean-up as well as the elimination of closed loop systems wherein nonapplied carrier-size formulation is returned to the supply receptacle. Of course, inasmuch as no aqueous or organic carriers are present within the formulations of the invention, economies are realized through the substantial elimination of thermal energy otherwise required in oven drying. Further, the lower volumes involved lessen "sling-off" of size product from moving strands otherwise leading to pollution problems. The lower quantities of size involved play a roll in permitting the substantial removal of volatile constituents prior to the filaments reaching the packaging spool.

As indicated earlier, the particular formulation of carrier-free size in accordance with the invention will depend upon the contemplated ultimate utilization of the coated glass fibers. Of these end uses, the size criteria associated with "weavers" roving applications may be deemed more technically demanding. Accordingly, formulations and the testing thereof with respect to that end use are addressed with more emphasis in the description to follow.

Looking to the principal components of size formulations, conventional size lubricants will include such materials as amine salts, animal and vegetable oils, silicone lubricants, the condensates of amines and fatty acids such as octadecyl amine acetate, polyethylene glycols and their esters and polypropylene glycols. Lubricant selection also will be made in conjunction with the integrity or relative stiffness of the strand as is desired by the operator. Of course, other factors, including the selection of film former, are associated with this stiffness characteristic.

The couplers utilized in connection with sizing operations usually are silanes or organosilanes. The organosilane may be defined as a silane having one or more alkyl, aryl, aryl-alkyl or alkyl-aryl group thereon which group includes a functional radical which contains an oxirane ring or that is reactive with a curing agent for an oxirane ring. Organosilicon compounds which are characterized by at least one organo group that includes an amino, epoxy, hydroxyl, chloro or thiol radical are suitable, as well as mixtures of two or more types of these compounds having different radicals. Suitable groups include: gamma amino propyl, N-methyl gamma amino propyl, N-phenyl gamma amino propyl, N,N-methyl gamma amino propyl, N-alkyl gamma amino propyl, N-beta(aminoethyl)gamma amino propyl, amino phenyl, the acrylic salt of N-beta(amino ethyl)gamma amino propyl, gamma methacryloxy, propyl, gamma glycidoxy propyl, beta(3,4 epoxy cyclohexyl)ethyl, beta(3,4 epoxy 4 methyl cyclohexyl)ethyl, 2 propyl-9,10 epoxystearate, copolymer of 1 part vinyl silane and 2 parts glycidyl methacrylate, copolymer of 2 parts vinyl silane and 1 part glycidyl methacrylate, 2:1 vinyl silane, gamma(2 hydroxyl phenyl)propyl, gamma(4 hydroxyl phenyl)propyl, formal derivative of gamma(3,4 dehydroxy phenyl)propyl, gamma hydroxyl propyl, gamma thiol propyl, amino biphenyl, benzimadzole substituted groups, alkyl cycloalkyl epoxides, cycloalkyl alkyl epoxides, alkyl epoxides, alkyl aryl epoxides, aryl alkyl epoxides, etc.

The film former component of the size formulations particularly is selected with respect to intended end use. These film formers accordingly will be selected from a broad variety of compounds. Typically, epoxy resins are utilized, for example, aliphatic and bisphenol A epoxy-based formulations. Alternately, polyester and polybutadiene formulations will be selected for elastomeric end use applications. Typical film former components will be revealed in the exemplary material to follow.

By using the above principal size components in the absence of an aqueous carrier, the physical, bulk quantity of size applied is reduced. Of the size thus applied, that moisture remaining on the fiber from the pre-pad cooling stage will hydrolyze silane coupling agents and those alcohol constituents will substantially vaporize as well as remaining moisture during the forming stages prior to reaching the packaging spool. Similarly, the blocking agent, such as acetone, will volatilize considerably in the forming process and the overall effect is the production of a strand package exhibiting a one to two percent by weight volatile constituent content. No solids migration occurs upon subsequent oven drying.

The following examples demonstrate the practice of the invention wherein aliphatic epoxy film former formulations are provided. In these examples and the examples to follow, the amounts indicated are expressed in parts by weight:

EXAMPLE 1

    ______________________________________                                                                   Parts By                                                                       Weight                                                                         (P.B.W.)                                             ______________________________________                                         Oleic acid                  42                                                 Cycloaliphatic epoxy (ERL 4221).sup.1                                                                      42                                                 Gamma-Methacryloxy-Propyl Triethoxy Silane (A174).sup.2                                                    16                                                 ______________________________________                                    

EXAMPLE 2

    ______________________________________                                                                   P.B.W.                                               ______________________________________                                         Oleic acid                  21                                                 Cycloaliphatic epoxy (ERL 4221).sup.1                                                                      63                                                 Gamma-Methacryloxy-Propyl Triethoxy Silane (A174).sup.2                                                    16                                                 ______________________________________                                    

EXAMPLE 3

    ______________________________________                                                              P.B.W.                                                    ______________________________________                                         Polyethylene glycol 400 Monooleate                                                                    42                                                      Cycloaliphatic epoxy (ERL 4221).sup.1                                                                 42                                                      Triethoxy Silane (A174).sup.2                                                                         16                                                      ______________________________________                                    

The following examples demonstrate size formulations according to the invention wherein polyester or polybutadiene compositions are incorporated as film former:

EXAMPLE 4

    ______________________________________                                                                   P.B.W.                                               ______________________________________                                         Diallyl phthalate           24                                                 E720.sup.3                  26                                                 Oleyl alcohol reacted with 5 moles of ethylene oxide                                                       25                                                 Benzoyl peroxide             1                                                 Triethoxy Silane (A174).sup.2                                                                              25                                                 ______________________________________                                    

EXAMPLE 5

    ______________________________________                                                              P.B.W.                                                    ______________________________________                                         Triethoxy Silane (A174).sup.2                                                                         32                                                      E400.sup.4             30                                                      Polyethylene glycol 400 Monooleate                                                                    32                                                      Amino silane (A1100).sup.5                                                                             8                                                      ______________________________________                                    

EXAMPLE 6

    ______________________________________                                                                   P.B.W.                                               ______________________________________                                         Gamma-Methacryloxy-Propyl Triethoxy Silane (A174).sup.2                                                    17                                                 Amino Silane (A1100).sup.5   8                                                 Polybutadiene (45H).sup.6   50                                                 Pentaerythritol fatty acid esters (Hercolube J15).sup.7                                                    25                                                 ______________________________________                                    

EXAMPLE 7

    ______________________________________                                                                   P.B.W.                                               ______________________________________                                         Oleyl alcohol reacted with 5 moles of ethylene oxide                                                       25                                                 Gamma-Methacryloxy-Propyl Triethoxy Silane (A174).sup.2                                                    17                                                 Amino Silane (A1100).sup.5   8                                                 Polybutadiene               50                                                 ______________________________________                                    

EXAMPLE 8

    ______________________________________                                                                   P.B.W.                                               ______________________________________                                         Gamma-Methacryloxy-Propyl Triethoxy Silane (A174).sup.2                                                    16                                                 Polyethylene glycol 400 Monooleate                                                                         16                                                 Amino Silane (A1100).sup.5   8                                                 E400.sup.4                  60                                                 ______________________________________                                    

EXAMPLE 9

    ______________________________________                                                                   P.B.W.                                               ______________________________________                                         Gamma-Methacryloxy-Propyl Triethoxy Silane (A174).sup.2                                                    16                                                 Polyethylene glycol 400 Monooleate                                                                         16                                                 Amino Silane (A1100).sup.5   8                                                 E500.sup.8                  60                                                 ______________________________________                                    

The following formulations are provided having a bisphenol A type epoxy film former component:

EXAMPLE 10

    ______________________________________                                                                   P.B.W.                                               ______________________________________                                         Epoxy resin (DER 330).sup.9 64                                                 Polyethylene glycol 400 Monooleate                                                                         9                                                  Polyethyleneimine           1                                                  Gamma-Methacryloxy-Propyl Triethoxy Silane (A174).sup.2                                                    17                                                 Amino Silane (A1100).sup.5  9                                                  ______________________________________                                    

EXAMPLE 11

    ______________________________________                                                                   P.B.W.                                               ______________________________________                                         Epoxy resin (DER 330).sup.9 60.0                                               Polyethylene glycol 400 Monooleate                                                                         8.4                                                Polyethyleneimine           0.9                                                Gamma-Methacryloxy-Propyl Triethoxy Silane (A174).sup.2                                                    16.0                                               Amino Silane (A1100).sup.5  8.4                                                Acetic Acid                 6.7                                                ______________________________________                                    

EXAMPLE 12

    ______________________________________                                                                   P.B.W.                                               ______________________________________                                         Epoxy resin (DER 330).sup.9 61.8                                               Polyethyleneimine           0.9                                                Gamma-Methacryloxy-Propyl Triethoxy Silane (A174).sup.2                                                    16.5                                               Amino Silane (A1100).sup.5  8.7                                                Acetone                     3.5                                                Trylube 24/32.sup.10        8.7                                                ______________________________________                                    

EXAMPLE 13

    ______________________________________                                                                   P.B.W.                                               ______________________________________                                         Epoxy resin (DER 330).sup.9 41                                                 Gamma-Methacryloxy-Propyl Triethoxy Silane (A174).sup.2                                                    16                                                 Amino Silane (A1100).sup.5   8                                                 Ciba 906.sup.11             23                                                 Pluronic L101.sup.12         4                                                 Pluronic P105.sup.13         8                                                 ______________________________________                                    

EXAMPLE 14

    ______________________________________                                                                   P.B.W.                                               ______________________________________                                         Epoxy resin (DER 330).sup.9 41                                                 Gamma-Methacryloxy-Propyl Triethoxy Silane (A174).sup.2                                                    16                                                 Trylube 24/32.sup.10        10                                                 Ciba 906.sup.11             25                                                 Diamino methoxy silane (Z6020).sup.14                                                                       8                                                 ______________________________________                                    

EXAMPLE 15

    ______________________________________                                                                   P.B.W.                                               ______________________________________                                         Epoxy resin (DER 330).sup.9 50                                                 Gamma-Methacryloxy-Propyl Triethoxy Silane (A174).sup.2                                                    17                                                 Amino Silane (A1100).sup.5  8                                                  Acetone                     4                                                  Trylube 24/32.sup.10        5                                                  Oleyl alcohol reacted with 5 moles of ethylene oxide                                                       15                                                 Versamid 140.sup.15         5                                                  ______________________________________                                    

EXAMPLE 16

    ______________________________________                                                                   P.B.W.                                               ______________________________________                                         Epoxy resin (DER 330).sup.9 65                                                 Acetone                      6                                                 Versamid 140.sup.15         10                                                 Gamma-Methacryloxy-Propyl Triethoxy Silane (A174).sup.2                                                    17                                                 Amino Silane (A1100).sup.5   8                                                 ______________________________________                                    

EXAMPLE 17

    ______________________________________                                                          P.B.W.                                                        ______________________________________                                         Epoxy resin (DER 330).sup.9                                                                       74.3                                                        Z6071.sup.16       14.3                                                        Dioctyl Phthlate   11.4                                                        ______________________________________                                    

EXAMPLE 18

    ______________________________________                                                                   P.B.W.                                               ______________________________________                                         Epoxy resin (DER 330).sup.9 55                                                 Acetone                      4                                                 Versamid 140.sup.15         10                                                 A151.sup.17                 20                                                 Trylube 24/32.sup.10         5                                                 Oleyl alcohol reacted with 5 moles of ethylene oxide                                                       10                                                 ______________________________________                                    

EXAMPLE 19

    ______________________________________                                                                   P.B.W.                                               ______________________________________                                         Epoxy resin (DER 330).sup.9 45                                                 Acetone                      4                                                 Versamide 140.sup.15        10                                                 Dioctyl Phthalate           10                                                 A151.sup.17                 20                                                 Trylube 24/32.sup.10         5                                                 Oleyl alcohol reacted with 5 moles of ethylene oxide                                                       10                                                 ______________________________________                                    

EXAMPLE 20

    ______________________________________                                                                   P.B.W.                                               ______________________________________                                         Epoxy resin (DER 337).sup.18                                                                               66                                                 Trylube 24/32.sup.10        16                                                 Gamma-Methacryloxy-Propyl Triethoxy Silane (A174).sup.2                                                    16                                                 Epoxy Silane (A187)          8                                                 ______________________________________                                    

EXAMPLE 21

    ______________________________________                                                                   P.B.W.                                               ______________________________________                                         Epoxy resin (DER 330).sup.9 45                                                 Shell Hardner H3.sup.20     10                                                 Versamid 140.sup.15         10                                                 A151.sup.17                 20                                                 Oleyl alcohol reacted with 5 moles of ethylene oxide                                                       10                                                 Trylube 24/32.sup.10         5                                                 ______________________________________                                    

EXAMPLE 22

    ______________________________________                                                                   P.B.W.                                               ______________________________________                                         Epoxy resin (DER 330).sup.9 67                                                 Gamma-Methacryloxy-Propyl Triethoxy Silane (A174).sup.2                                                    21                                                 Amino Silane (A1100).sup.5  4                                                  Oleyl alcohol reacted with 5 moles of ethylene oxide                                                       5                                                  Ethox CAM15.sup.21          5                                                  Versamid 140.sup.15         3                                                  Acetone                     3                                                  ______________________________________                                    

EXAMPLE 23

    ______________________________________                                                                   P.B.W.                                               ______________________________________                                         Epoxy resin (DER 330).sup.9 54.7                                               Oleyl alcohol reacted with 5 moles of ethylene oxide                                                       14.2                                               Ethox CAM15.sup.21           1.9                                               Gamma-Methacryloxy-Propyl Triethoxy Silane (A174).sup.2                                                    16.0                                               Amino Silane (A1100).sup.5   7.5                                               Acetone                      5.7                                               ______________________________________                                    

EXAMPLE 24

    ______________________________________                                                                   P.B.W.                                               ______________________________________                                         Epoxy resin (DER 330).sup.9 53                                                 Oleyl alcohol reacted with 5 moles of ethylene oxide                                                       10                                                 Trylube 24/32.sup.10        5                                                  Versamid 140.sup.15         7                                                  Gamma-Methacryloxy-Propyl Triethoxy Silane (A174).sup.2                                                    17                                                 Amino Silane (A1100).sup.5  8                                                  Acetone                     5                                                  ______________________________________                                    

EXAMPLE 25

    ______________________________________                                                                   P.B.W.                                               ______________________________________                                         Epoxy resin (DER 330).sup.9 41                                                 Ciba 906.sup.11             25                                                 Trylube 24/32.sup.10        10                                                 Gamma-Methacryloxy-Propyl Triethoxy Silane (A174).sup.2                                                    16                                                 Amino Silane (A1100).sup.5   8                                                 ______________________________________                                    

EXAMPLE 26

    ______________________________________                                                                   P.B.W.                                               ______________________________________                                         Epoxy resin (DER 330).sup.9 64                                                 Polyethylene glycol 400 Monooleate                                                                         9                                                  Gamma-Methacryloxy-Propyl Triethoxy Silane (A174).sup.2                                                    17                                                 Amino Silane (A1100).sup.5  9                                                  Polyethyleneimine           1                                                  ______________________________________                                    

EXAMPLE 27

    ______________________________________                                                                   P.B.W.                                               ______________________________________                                         Epoxy resin (DER 330).sup.9 60.0                                               Ethox CAM15.sup.21           2.5                                               Oleyl alcohol reacted with 5 moles of ethylene oxide                                                       12.5                                               Triethoxy Silane (A174).sup.2                                                                              19.0                                               Amino Silane (A1100).sup.5   6.0                                               Acetone                      3.0                                               ______________________________________                                    

EXAMPLE 28

    ______________________________________                                                                   P.B.W.                                               ______________________________________                                         Epoxy resin (DER 330).sup.9 60.0                                               Ethox CAM15.sup.21           2.5                                               Oleyl alcohol reacted with 5 moles of ethylene oxide                                                       12.5                                               Triethoxy Silane (A174).sup.2                                                                              21.0                                               Amino Silane (A1100).sup.5   4.0                                               Acetone                      2.0                                               ______________________________________                                    

EXAMPLE 29

    ______________________________________                                                                   P.B.W.                                               ______________________________________                                         Epoxy resin (DER 330).sup.9 60.0                                               Ethox CAM15.sup.21           2.5                                               Oleyl alcohol reacted with 5 moles of ethylene oxide                                                       12.5                                               Triethoxy Silane (A174).sup.2                                                                              23.0                                               Amino Silane (A1100).sup.5   2.0                                               Acetone                      1.0                                               ______________________________________                                    

EXAMPLE 30

    ______________________________________                                                                   P.B.W.                                               ______________________________________                                         Epoxy resin (DER 330).sup.9 63.0                                               Ethox CAM15.sup.21           2.5                                               Oleyl alcohol reacted with 5 moles of ethylene oxide                                                       12.5                                               Triethoxy Silane (A174).sup.2                                                                              17.0                                               Amino Silane (A1100).sup.5   5.0                                               Acetone                      6.0                                               ______________________________________                                    

EXAMPLE 31

    ______________________________________                                                                   P.B.W.                                               ______________________________________                                         Epoxy resin (DER 330).sup.9 63.0                                               Ethox CAM15.sup.21           2.5                                               Oleyl alcohol reacted with 5 moles of ethylene oxide                                                       12.5                                               Triethoxy Silane (A174).sup.2                                                                              17.0                                               Amino Silane (A1100).sup.5   5.0                                               Acetone                      6.0                                               ______________________________________                                    

EXAMPLE 32

    ______________________________________                                                          P.B.W.                                                        ______________________________________                                         Epoxy resin (DER 330).sup.9                                                                       60.0                                                        Polyethyleneimine  0.9                                                         Trylube 24/32.sup.10                                                                              8.4                                                         Triethoxy Silane (A174).sup.2                                                                     16.0                                                        Amino Silane (A1100).sup.5                                                                        8.4                                                         ______________________________________                                    

EXAMPLE 33

    ______________________________________                                                          P.B.W.                                                        ______________________________________                                         Epoxy resin (DER 330).sup.9                                                                       60.0                                                        Polyethyleneimine  0.9                                                         Acetic Acid        6.7                                                         Trylube 24/32.sup.10                                                                              8.4                                                         Triethoxy Silane (A174).sup.2                                                                     16.0                                                        Amino Silane (A1100).sup.5                                                                        8.4                                                         ______________________________________                                    

EXAMPLE 34

    ______________________________________                                                             P.B.W.                                                     ______________________________________                                         Epoxy resin (DER 330).sup.9                                                                          41                                                       Ciba 906.sup.11       25                                                       Trylube 24/32.sup.10  10                                                       Triethoxy Silane (A174).sup.2                                                                        16                                                       Diamino Methoxy Silane (Z6020).sup.22                                                                 8                                                       ______________________________________                                    

EXAMPLE 35

    ______________________________________                                                                   P.B.W.                                               ______________________________________                                         Epoxy resin (DER 330).sup.9 50                                                 Acetone                     4                                                  Trylube 24/32.sup.10        5                                                  Versamid 140.sup.15         5                                                  Oleyl alcohol reacted with 5 moles of ethylene oxide                                                       15                                                 Gamma-Methacryloxy-Propyl Triethoxy Silane (A174).sup.2                                                    17                                                 Amino Silane (A1100)        8                                                  ______________________________________                                    

EXAMPLE 36

    ______________________________________                                                                   P.B.W.                                               ______________________________________                                         Epoxy Resin (DER 330).sup.9 50                                                 Acetone                      6                                                 Trylube 24/32.sup.10         5                                                 Versamid 140.sup.15         10                                                 Oleyl alcohol reacted with 5 moles of ethylene oxide                                                       10                                                 Gamma-Methacryloxy-Propyl Triethoxy Silane (A174).sup.2                                                    17                                                 Amino Silane (A1100).sup.5   8                                                 ______________________________________                                    

EXAMPLE 37

    ______________________________________                                                                   P.B.W.                                               ______________________________________                                         Epoxy resin (DER 330).sup.9 65                                                 Acetone                      6                                                 Versamid 140.sup.15         10                                                 Gamma-Methacryloxy-Propyl Triethoxy Silane (A174).sup.2                                                    17                                                 Amino Silane (A1100).sup.5   8                                                 ______________________________________                                    

EXAMPLE 38

    ______________________________________                                                                   P.B.W.                                               ______________________________________                                         Epoxy resin (DER 330).sup.9 59.7                                               Polyethylene glycol 400 Monooleate                                                                         8.4                                                Gamma-Methacryloxy-Propyl Triethoxy Silane (A174).sup.2                                                    15.9                                               Amino Silane (A1100).sup.5  8.4                                                Polyethyleneimine           0.9                                                                            6.7                                                ______________________________________                                    

EXAMPLE 39

    ______________________________________                                                                   P.B.W.                                               ______________________________________                                         Epoxy resin (DER 332)       65                                                 Polyethylene glycol 400 Monooleate                                                                          9                                                 Gamma-Methacryloxy-Propyl Triethoxy Silane (A174).sup.2                                                    17                                                 Amino Silane (A1100).sup.5   9                                                 ______________________________________                                    

EXAMPLE 40

    ______________________________________                                                                   P.B.W.                                               ______________________________________                                         Epoxy resin (DER 332).sup.23                                                                               63                                                 Polyethylene glycol 400 Monooleate                                                                         19                                                 Gamma-Methacryloxy-Propyl Triethoxy Silane (A174).sup.2                                                    12                                                 Amino Silane (A1100).sup.5   6                                                 ______________________________________                                    

EXAMPLE 41

    ______________________________________                                                                   P.B.W.                                               ______________________________________                                         Epoxy resin (DER 330).sup.9 64                                                 Igepal 630.sup.24           8                                                  Trylube 7607.sup.25         2                                                  Gamma-Methacryloxy-Propyl Triethoxy Silane (A174).sup.2                                                    16                                                 Amino Silane (A1100).sup.5  6                                                  Acetone                     4                                                  ______________________________________                                    

EXAMPLE 42

    ______________________________________                                                                   P.B.W.                                               ______________________________________                                         Epoxy resin (DER 330).sup.9 61.3                                               Igepal 630.sup.24           7.7                                                Trylube 7607.sup.25         1.9                                                Gamma-Methacryloxy-Propyl Triethoxy Silane (A174).sup.2                                                    15.3                                               Amino Silane (A1100).sup.5  5.7                                                Diacetone alcohol           8.0                                                ______________________________________                                    

Generally, the coupler component of the size formulation will be present in an amount between about 5-30 percent by weight, the lubricant will be present in an amount between about 10-65 percent by weight, and the film former will be present in an amount between about 10-70 percent by weight. A typical procedure utilized in preparing those sizes incorporating a blocking agent, e.g. acetone, provides for the separate mixing of blocking agent with coupling agent, e.g. amino silane, as well as the separate mixing of the remaining film former and lubricant components. The resultant two mixtures then are added together with moderate agitation. The blocking agent will be present in an amount corresponding with the amino silane coupler content and will generally be present in an amount less than about eight percent by weight.

Glass fiber packages having been treated with size in accordance with the invention wherein no aqueous or organic fluid carrier per se is utilized and the volatile blocking constituent of the size formulations is held below about eight percent by weight, when formed into packages, have exhibited essentially no migratory effects. Some migration may be developed due to the centrifugal action of the winding of the strand, however, such effects are dismissable in extent. While migratory effects can be physically observed at the surface of strand packages, the data set forth in Tables 1 and 2 demonstrate the essential uniformity of size application from the inside of the outside of a strand package following the treatment of the fibers thereof with the sizes identified above as Example 40, 41 and 42. The technique developing the data is one wherein successive equal quantities of the strand are removed from the package commencing with the inside thereof and each quantity is subjected to a loss on ignition (LOI) evaluation. To provide the package utilized in connection with Table 1, the sizes were applied to glass fibers using a roll-type applicator, following which the fibers were grouped together into a strand and the strand was wrapped upon a revolving mandrel to produce the package. Commencing with the innermost portion of the package, successive 900 gram lengths (Table 1) of the strand or successive pounds of strand (Table 2) were removed and the amount of size upon a predetermined quantity thereof determined by placing the samples in a muffle furnace at about 1200° F. for 20 minutes to burn the coating therefrom. The ignition loss percent (LOI) then was calculated by comparing the weight of the skein before and after burning. A demonstration of the lack of migration in the package is shown in Tables 1 and 2 by virtue of the relative consistent LOI percentages from the inside to the outside of the package. A comparison of the above with typical migratory effects encountered with other sizes, for example, a conventionally utilized water-carried size, may be provided by comparing the computed ratio of the "outside" LOI values with respect to the nominal LOI values at the center of the package evaluated. These "migration ratios" for sizes incorporating aqueous carrier (95% by weight carrier) range in value from about four to six. As evidenced by Tables 1 and 2, the migration ratios developed utilizing size formulations according to the invention remain very close to desired unity. The parallel tensile and knot tensile data given in Table 1 show that the individual glass fibers within the evaluated package exhibit industrially acceptable strengths under a conventional test technique therein parallel disposed fibers are stressed to breakage with and without a simple forehand knot formed therein.

                  TABLE 1                                                          ______________________________________                                         WEIGHT OF PACKAGE                                                                              LOI    PARALLEL*   KNOT*                                       GMS             %      TENSILE     TENSILE                                     ______________________________________                                         14,760   (Inside)   .55    129       37                                        13,860              .56    122       37                                        12,960              .63    116       39                                        12,060              .57    116       39                                        11,160              .54    117       41                                        10,260              .62    123       37                                        9,360               .60    113       38                                        8,460               .60    102       38                                        7,560               .55    111       39                                        6,660               .52    106       40                                        5,760               .59    130       35                                        4,860               .52    127       43                                        3,960               .66    110       35                                        3,060               .42    121       38                                        2,160               .43    107       38                                        1,260    (Outside)  .51    103       36                                        ______________________________________                                          *pounds                                                                  

                  TABLE 2                                                          ______________________________________                                         LOI PROFILE FROM INSIDE TO OUTSIDE OF PACKAGE                                  FORMULATION       FORMULATION                                                  EXAMPLE NO. 41    EXAMPLE NO. 42                                               WEIGHT OF             WEIGHT OF                                                PACKAGE               PACKAGE                                                  LBS.        % LOI     LBS.        % LOI                                        ______________________________________                                         INSIDE                INSIDE                                                   27      lbs.     .90      17    lbs.  .82                                      26               .94      16          .80                                      25               .97      15          .80                                      24               .98      14          .80                                      23              1.00      13          .79                                      22              1.01      12          .82                                      21              1.01      11          .73                                      20              1.01      10          .75                                      19              1.01      9           .80                                      18              1.02      8           .72                                      17              1.02      7           .83                                      16              1.02      6           .85                                      15              1.02      5           .80                                      14              1.02      4           .71                                      13              1.02      3           .73                                      12              1.02      2           .74                                      11              1.02      1           .82                                      10              1.01      OUTSIDE                                              9               1.01                                                           8               1.01                                                           7               1.01                                                           6               1.02                                                           5               1.03                                                           4               1.03                                                           3               1.03                                                           2               1.02                                                           1               1.03                                                           OUTSIDE                                                                        ______________________________________                                    

The application of the carrier-free sizes of the instant invention will vary in accordance with the particular desires of the user. Where the sizes are instantly mixed, i.e. formed at the point of application, no shelf life considerations are involved. Similarly, where materials are selected such that no reaction is evoked between the coupler and film former, shelf life is not a consideration. For many applications, however, it is necessary that the size formulations exhibit a shelf life of an extent acceptable to conventional industrial practice. With the instant invention, a volatile blocking agent is added to the formulation and driven from the wound package in part by conventional oven heating of relatively short duration. However, no migration phenomena are experienced inasmuch as the volatile blocking agent is added in an amount less than about eight percent. This constituent then vaporizes to a considerable extent in the forming process, one to two percent moisture being present in the "wet" package such that no capillary action takes place to physically drive the size formulation solids from their position of application during the heat drying stage. This maintenance of the deposition integrity of the size is evidenced by the LOI data of Table 2 where Examples 41 and 42 formulations were utilized respectively having an acetone blocking agent present in an amount of four percent by weight and a diacetone alcohol blocking agent in an amount of eight percent by weight.

Looking to Table 3, the effectiveness of acetone and acetic acid as blocking agents for the size formulations of the invention are revealed. Note that the viscosity of the blocking agent-containing formulations remains within acceptable limits for an interval suited to conventional industrial requirements. These data further reveal that both acetone and acetic acid perform acceptably, acetone generally being preferred. The viscosity preferred for coating sizes according to the invention will fall within the range of about 100 to 200 cps at 75° F., however viscosities as high as 2000 cps can be applied.

                  TABLE 3                                                          ______________________________________                                         VISCOSITIES (cps)                                                              Formulation Example No.                                                        Without Blocking Agent                                                                          With Blocking Agent                                           Day  #32       #34       #35  #33   #36  #37  #42                              ______________________________________                                         0      194     238        65  120    85  100  130                              1     2,945    546       125  397   200  370                                   2     7,080    836       140  --    250  550                                   3     8,100    950       165  --    340  884                                   4    --        --        200  --    435  884                                   5    --        --        --   740   --   --                                    6    --        --        --   1,100 --   --                                    7    12,340    2,072     --   --    --   --   196                              8    15,120    2,028     --   1,050 --   --                                    9    --        --        --   --    --   --                                    10   23,200    2,600     --   --    --   --                                    14                                            240                              21                                            310                              ______________________________________                                    

In the discourse to follow, evidence is provided showing that the size formulations of the invention perform at least equivalently with conventional carrier-containing sizes in all essential applications. This evidence includes a broad range of tests as well as size formulations portions of the data being compiled in conjunction with corresponding tests utilizing an industrially accepted aqueous carrier containing size (about 95% by weight carrier) identified as "Std."

Looking to Table 4, the results of flexural strength, tensile strength and compressive strength testing under ASTM D2150-70 of samples of woven roving laminated within a polyester resin are revealed. The laminates were formed of four layers of woven roving sized with the formulations identified and having 14×14 inch square shape. The layers were impregnated in an unpromoted orthophthalic polyester resin with low styrene content marketed by Owens Corning Fiberglas Co. under the trade designation, "E410". Following impregnation the layers were pressed at a total pressure of 10 p.s.i. to form each sample. The samples were then cut into predetermined shapes for testing. In this regard, the designation, 0°, indicates testing in the weaving machine direction of the fabric, while the designation, 90°, indicates testing in a direction transverse to machine direction. The data reveal that the laminates sized in accordance with the teachings of the invention performed comparably with samples treated with a standard aqueous carrier containing and identified as "Std."

                  TABLE 4                                                          ______________________________________                                         Size Formulation                                                               Example No.   26      Std.    24   27    Std.                                  ______________________________________                                         Flexural Strength                                                              psi × 10.sup.3                                                           Dry 0° 74.3    62.0    63.5 63.2  51.4                                  Dry 90°                                                                               71.9    63.0    55.3 55.0  41.8                                  Boiled 2 hrs. 0°                                                                      65.0    53.8    45.2 57.7  43.5                                  Boiled 2 hrs 90°                                                                      70.1    54.7    41.4 48.9  39.4                                  Tensile Strength                                                               Dry           44.4    46.1    41.0                                             Boiled        38.3    42.7    --                                               Compressive Strength                                                           Dry           32.6    31.9    31.1                                             Boiled        35.9    29.7    --                                               ______________________________________                                    

Another test procedure provides for the fabrication of glass fiber retaining rods which are then tested for flexural strength. To provide the test specimen rods, glass fibers are formed and treated with a selected size. Following this treatment, the fibers are drawn together to form a strand which is coiled into a package and dried as described above. A plurality of these strands of predetermined weight is then immersed within a predetermined resin solution, following which the resin-coated strands are pulled through glass tubing which removes excess resin and shapes the impregnated strands into the form of a rod. The resin forming the rods is then cured for one hour at 235° F. and flexural strength test procedures are carried out. Following preparation, a given number, usually half, of the specimens are boiled for 24 hours prior to testing. Test procedures are carried out under controlled environmental temperature and humidity conditions, the boiled and unboiled specimens being stressed in flexure at predetermined rates by a conventional constant cross-head machine to failure. Tables 5 and 6 provide flexural strength data for rods fabricated utilizing glass fibers treated in accordance with the method of the invention and utilizing the formulations indicated. The rods formed for developing the data were fabricated utilizing a resin provided as a mixture of 100 parts by weight polyester resin marketed under the trade designation "E 701" by Owens Corning Fiberglas Corp., five parts by weight styrene and one part by weight benzoyl peroxide. Additionally, comparative data is provided in the tables wherein rods are identically formed but utilizing glass fibers treated with the above-described standard size (Std.). The data in these tables reveal that specimen rods fabricated utilizing the size formulations of the invention perform comparably with rods fabricated utilizing conventionally-sized glass fibers.

                  TABLE 5                                                          ______________________________________                                         Size Formulation                                                               Example No. 27     28     29   30   Std. 26*  39                               ______________________________________                                         Flexural Strength                                                              dry, psi × 10.sup.3                                                                  188    176    175  191  171  239  211                              boiled, psi × 10.sup.3                                                               175    164    162  175  157  207  174                              LOI percentage                                                                             31.6   30.5   31.3 30.1 32.0  31   36                              ______________________________________                                          *No oven treatment                                                       

                  TABLE 6                                                          ______________________________________                                                      25      25            26    26                                    Size Formulation                                                                            1.1%    2.0%          0.89% 1.0%                                  Example No.  LOI     LOI     Std.  LOI   LOI                                   ______________________________________                                         Flexural Strength                                                              psi × 10.sup.3                                                           dry          178.5   175.9   184.1 180.7 200.2                                 boiled 24 hours                                                                             157.6   155.6   154.9 167.2 177.3                                 Average Diameter                                                                            0.146   0.146   0.146 0.149 0.148                                 (inches)                                                                       LOI percentage                                                                              29.29   26.33   29.71                                             ______________________________________                                    

Another test utilized in evaluating glass fiber reinforcement is known as the Naval Ordinance Laboratory (NOL) test wherein rings are made according to ASTM specification D-2291 and are tested according to ASTM specification D-2344-72. As in the case of rod specimens, the NOL rings may be formed utilizing a variety of resin binders.

Still another test procedure looks to the tendency for the glass fiber material to form fuzz as described earlier herein. The assignee of the present invention has developed an abrasion test for evaluating the amount of fuzz produced by fibers. This test involves the passing of glass fiber strands through a predetermined number of mutually spaced ceramic eyelets which are arranged such that the strand undergoes directional changes when moving from eyelet to eyelet. Upon passing these contact points, the strand passes through a collection box and then to a metering wheel and to a wrap reel. The amount of fuzz accumulated for a given weight of strand is weighed and reported as the fuzziness of the strand. The test is carried out under controlled environmental conditions.

Referring to Table 7, NOL ring tests data for rings formed with an epoxy amine binder as well as with the above-described polyester binder (E701) are set forth. The table further includes flexural strength data for rod specimens formed with polyester binder as well as fuzz data. These data are compiled for test specimens formed with strand sized with the formulation of example 24 and exhibiting a series of six LOI values as well as for standard "Std." size treated glass fibers. Additionally included in the data is the LOI value for the resin binder as well as a percent retention. The LOI value for resin binder indicates the amount of organic resin burned off the sample, while the percent retention is the ratio of the strength of the boiled specimens (24 hour) to that of the dry specimens. As in the above-described test, the data represented in Table 7 shows that the size treatment of the instant invention produces comparable results with the standard, aqueous carrier containing size. Additionally, it may be noted that the 7-point and 11-point (ceramic rings) values for fuzz production show the size materials of the instant invention to be of acceptable quality. The term "breakout" in the tabulation indicates that the strand speciment laterally breaks and the test is not completed.

Another test serving to evaluate the performance of the size treatment of the invention is identified as ASTM specification D2143 and involves the formation of filament-wound pipe and subsequent cyclic pressurization of the interior thereof with a liquid electrolyte until such time as electrical conductivity is detected through the pipe wall. In general, the pipe is formed by drawing strand from an appropriately size treated package through a resin bath, then through the guide eyes of a filament winding apparatus incorporating a mandrel.

                  TABLE 7                                                          ______________________________________                                         Size Formulation                                                                           .70%     .51%     .32%   .55% LOI                                  Example No. 24                                                                             LOI      LOI      LOI    Std.                                      ______________________________________                                         E701 PE RODS                                                                   Flexural Strength                                                              psi × 10.sup.3                                                           Dry         199.8    201.7    193.1  192.7                                     Boiled 24 hrs.                                                                             191.6    186.7    185.8  174.9                                     LOI         30.9     32.1     31.2   29.5                                      % Retention 95.9     92.6     96.2   90.8                                      E701 RINGS                                                                     Ring Shear                                                                     psi × 10.sup.3                                                           Dry         9.50     9.98     10.40  9.90                                      Boiled 24 hrs.                                                                             9.42     9.54     9.90   9.80                                      LOI         31.7     32.2     32.4   25.9                                      % Retention 99.2     95.6     95.2   99.0                                      EPOXY AMINE                                                                    RINGS                                                                          Ring Shear                                                                     psi × 10.sup.3                                                           Dry         8.36     8.42     8.80   8.65                                      Boiled 24 hrs.                                                                             8.01     7.30     8.25   7.78                                      LOI         26.6     24.8     23.3   20.3                                      % Retention 95.8     86.7     93.8   89.9                                      FUZZ                                                                            7 pt.                          5 ± 1.7                                                                          86.9 ± 44.5                            11 pt.      35 ± .5                                                                              45 ± 33                                                                              31 ± 30                                                                            Break Out                                 ______________________________________                                    

Generally, the winding from the guide eyes upon the mandrel is at a helix angle of 54° and the assembly provides a pipe having an inside diameter of 2.235 inches and a wall thickness of 0.075 inches. The resultant filament wound material is cured within an oven, for example at 275° F. for one hour.

The weeping of filament wound pipe is believed attributed to a fatigue failure between the laminating resin and the glass fiber reinforcement which evokes cracks in the now unreinforced laminating resin. In order to attain an improvement in this form of cycle to weep test, therefore, either a stronger bond must be produced between the laminating resin and the glass fiber reinforcement or a reduction in the number of broken glass filaments must be provided in the roving. The quality of the size thus plays an important role in achieving improved values for this test, and for the instant purpose, serves as a valuable comparative tool for evaluating the size of the instant invention with size treatments conventionally utilized and generally incorporating aqueous carriers.

Looking to the drawing, curves 10, 12 and 14 represent data developed from the treating of glass fiber reinforced pipes fabricated utilizing a vinyl ester resin marketed by Dow Chemical Co. under the trade designation "Derakane 411-45". Curve 10 represents data developed from pipes wound with glass fibers sized utilizing the formulation of Example 38, while curves 12 and 14 represent corresponding data developed from pipes wound with glass fiber treated with a standard aqueous carreir containing size. In developing the data, the specimen pipes were stressed as above-described at 25 cpm until weeping terminated each test. Hoop stresses relating median diameter, pressure asserted and pipe thickness were calculated in accordance with ASTM D1599-69.

It will be apparent that various changes and modifications can be made in the details of procedure, formulation and use without departing from the spirit of the invention, especially as defined in the following claims.

FOOTNOTES

    H.sub.2 NCH.sub.2 CH.sub.2 Si(OCH.sub.2 CH.sub.3 CH.sub.3).sub.3

marketed by Union Carbide Corporation. 

What is claimed is:
 1. A method of treating glass fibers which comprises depositing on the glass fibers a size comprising from about 5 to about 30 percent by weight of a silane coupler, from about 10 to about 65 percent by weight of a lubricant, from about 10 to about 70 percent by weight of an epoxy film former and an amount, up to about 8 percent by weight, of a volatile blocking agent sufficient for blocking the reaction of said coupler and said film former, said size having a viscosity not greater than 2000 cps and carrier being substantially absent therefrom.
 2. The method of claim 1 in which said blocking agent is acetone.
 3. The method of claim 1 wherein said size exhibits a viscosity within the range of about 100 to 200 cps at 75° F.
 4. The method of claim 1 in which said coupler is an amino silane.
 5. The method of claim 1 in which said blocking agent is substantially volatilized prior to package formation.
 6. The method of claim 1 in which said glass fibers are gathered as a package and said package is oven dried.
 7. The method of claim 6 in which the moisture content of the oven dried package is about one to two percent by weight.
 8. The method of claim 1 in which said epoxy film former is a bisphenol A epoxy-based resin. 